D. Purwaningsih, R. Roto, H. Sutrisno
This study aims to synthesis the Ni-doped LiNixMn2-xO4 (x = 0; 0.02; 0.04; 0.06; 08; 0.1) by low temperature solid-state reaction. The microstructure of the product was evaluated based on the mole ratio of Ni/Mn of the precursors. The structural analysis of LiNixMn2-xO4 was analyzed by x-ray diffraction equipped with the Direct Method of win PLOTR package program and Diamond. It was found that doping with Ni could change the size, crystallinity and microstructure of LiNixMn2-xO4. The LiNixMn2-xO4 solids have a cubic structure with a space group of Fd3m. The increase in the doping content does not affect the structure. The particle size of the products is about 150-500 nm. The crystallinity of the solids tends to increase with the increase in Ni content. However, the increase of Ni content in the product causes the lattice parameters of the unit cell to decrease. © Published under licence by IOP Publishing Ltd.
Department of Chemistry, Faculty of Mathematics and Natural Sciences, Gadjah Mada University, Sekip Utara BLS 21, Yogyakarta, 55584, Indonesia; Department of Chemistry Education, Faculty of Mathematics and Natural Sciences, Yogyakarta State University, Jl. Colombo 1, Yogyakarta, 55281, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock